Microcrystalline stone is in the form of granite conditions similar to the high temperature state, sintered through a special process, the texture is uniform, density, high hardness, compression, bending, impact resistance and other performance better than natural stone, durable, not easy to damage, not natural stone common fine crack.

Stone is a kind of microcrystalline stone products, it is natural marble, shell, glass, Mosaic as the main raw materials, with high quality polymer as binder, through advanced manufacturing technology refined green building materials.

As a result of the stone in the process of accurate screening, almost completely removed the radioactive material contained in the stone, and after the high pressure of high performance binder bonding, more make its purpose increased, some strength even higher than natural stone.In the synthesis process, the use of concentrated ingredients technology, completely solve the problem of color difference in the process of natural stone decoration without support, especially suitable for large area pavement in the project.Natural marble is in processing process, because of the limitation of stone material itself, the size that the client can follow plank processing only, and cannot be decided with oneself design.And gang stone plate size is large, there are 3050×1250×12mm ultra-thin plate, this is the natural stone can not be compared with it.

The production process is as follows: ores → broken into gravel with different particle sizes → adding special raw material formula of granite → mixing and stirring → cloth → forming into square materials after vacuum gaocun → diamond row saw → wool plate → scraping and thickness determination → fine grinding and polishing → vertical and horizontal cutting machine → finished products

I. matters needing attention before construction include

1.In the process of transportation and handling, rolling and collision should be avoided to cause plate surface crack or damage;Outdoor stacking, should be covered with tarps to prevent rain, snow wet.

2.During installation, the cement mortar should not be too wet. Too wet cement mortar will cause two problems:

(1) a layer of water and gas film may be produced, resulting in the failure of firm bonding between granite and cement sand layer;

(2) water in the plate is difficult to evaporate, continue to alkalize with the cement, leading to erosion of the plate even crack.

3.Cement mortar must be mixed evenly, mixed uneven mortar itself poor structure, in addition to poor adhesion, in case of load may crack and damage the stone plate.